Description
Basic coated electrode for hardfacing parts on earth and mineral machines, impact drilling and crushing devices, springs, bucket edged and teeth as well as other materials required to have high resistance to wear.
Features and Applications
Applicable in final layer hardfacing of parts of earth and mineral mining machines, impact drilling and crushing devices, guide springs, edges of cutting tools, hard manganese steels, bucket edges and teeth, all of which are made of alloyed or unalloyed steels, as well as in other materials required to have high resistance to wear
Electrode of basic type with thick coating
lnclusion of chromium-silicon alloy, very hard electrode
Weld metal with ductile and cracking resistant behaviours: Crack resistance to impact force due to its high ductility: Machinability of weld metal through grinding only
It is recommended to pre-heat at 200-300°C for welding thick work pieces and materials tending to get hardened: Requirement of 2-3 layers hardfacing to obtain the highest resistance to wear
Suitable for harder and/or higher quality steels to buffer layering with the GeKa electrodes LASER B 50, TEMPO B 63, or, in some cases, with the GeKa electrodes such as ELOX B307, ELOX R 312
Requirement of re-drying for min. 2 hours at temperatures of 300°C
Standards | Current Type |
EN 14700 – E Fe 8 | D.C. (+) |
DIN 8555 – E6UM-60P |
Chemical Composition of Weld Metal % (Typical) | |||||
C | Cr | Si | |||
0.5 | 9.0 | 1.8 |
Mechanical Properties | |||
Weld Metal Hardness (HRC) | Soft Annealing (ºC) |
Hardening (ºC) |
Tempered (ºC) |
54 – 58 | 780 – 820 Slow Cooling Furnace |
1000 – 1050 in Oil |
300 – 400 |
Welding Positions
Operating Data | |||
Diameter x Length (mm) | Welding Current (A) | Package Weight (Kg) |
Carton Weight (Kg) |
3.20 x 350
4.00 x 450 5.00 x 450 |
100 – 140
140 – 180 180 – 230 |
5
6 6 |
15
18 18 |
Liability: Whilst all reasonable efforts have been made to ensure the accuracy of the information contained. This information is subject to change without notice and can be only considered as suitable for general guidance.